Rubber low temperature brittleness tester TRBT-A10 measures the highest temperature when vulcanized rubber is damaged due to an impact from test conditions, this temperature is called as brittle temperature. It identifies the difference between non-rigid plastic, flexible materials under low temperature. It also measures the brittle & low temperature performance quality of different types of vulcanized rubber materials.
| Temperature range | -60°C to 0°C |
| Temperature accuracy | ± 0.5°C |
| Impact speed | 2 m/s ± 0.2 m/s |
| Temperature fluctuation | <± 0.5°C |
| Distance between center of impact or bottom of gripper | 11 ± 0.5 mm |
| Outer dimension | 720×700×1380 mm |
| Cold well volume | 700 ml |
| Power | 1100 W |
| Net weight | 180 kg |
- Analogue display to observe temperature value
- -60°C to 0°C low temperature range
- Indications for highest temperature/brittleness test temperature
- Tests vulcanized rubber & other vulcanized material
Rubber low temperature brittleness tester has applications in scientific research testing, quality analysis, inspection units to measure highest temperature of vulcanized rubber & other materials.
Rubber Testing Instruments
Three roll mill machine TRMM-A10
- Mixed capacity
- 0.5 to 1 kg, 2 to 3 kg, 5 to 7 kg
- Temperature range
- RT to 300°C
- Temperature control system
- PID control
Rubber-weiss plasticity testing machine TRWM-A10
- Temperature range
- RT 50° to 300°
- Temperature accuracy
- ± 1°
- Measuring range
- 0.01 to 25 mm
Mooney viscometer TMV-A10
- Control temperature range
- Normal temperature to 200°C
- Temperature display resolution
- 0.01°C
- Temperature control accuracy
- ± 0.3°
No rotor rheometer TNRR-A10
- Temperature tester
- Room temperature to 200°C
- Temperature display resolution
- 0.1°C
- Temperature control accuracy
- ≤ ± 0.3°C
Paper Testing Instruments
Mullen burst tester TP-K10
- Measurement range
- 0 to 5600 kPa
- Accuracy
- ± 0.5 % F.S.
- Compression speed
- 170 ± 15 ml/min
Automatic horizontal tensile tester TP-B12
- Sample (size) length
- 180 mm (180, 150, 100, 90, 50 mm adjustable)
- Sample width
- 15 mm
- Measuring range
- 0 to 30, 0 to 100 N,0 to 300 N, 0 to 500 N, 0 to 1000 N
Puncture strength tester TP-J12
- Measuring range
- A (1 to 6) J indicating error ± 0.05 J B (1 to 12) J indicating error ± 0.05 J C (1 to 24) J indicating error ± 0.05 J D (1 to 48) J indicating error ± 0.05 J The indicating errors w.r.t measurement range of 20 to 80 %
- Frictional resistance
- Pyramid dimension
- Three sides: 60×60×60 mm, height 25 ± 0.7 mm, Arris edge fillet radius 1.5 ± 0.1 mm
Plastic Testing Instruments
Falling Weight Impact Tester TFWT-A10
- Temperature range
- 10 to 35°C
- Maximum falling height
- 2000 mm
- Resolution of displacement
- 1 mm
Primary adhesive tester TPAT-A10
- Inclined adjustable angle
- 0 to 40°
- Panel width
- 120 mm
- Test area width
- 80 mm
Melt flow Indexer TMFI-A11
- Measuring range
- 0.01to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm3/ 10 min (MVR), 0.001 to 9.999 g/ cm3 (melt density)
- Measuring rate
- 0.001 S
- Temperature range
- 50 to 400°C
NDT Testing Instruments
Digital Brinell hardness Tester TDBH-A10
- Test force
- 612.5 N, 980 N, 1225 N
- Brinell hardness test
- 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
- Hardness measuring area
- 8 to 650 HBW (hard metals steel ball)
Rockwell hardness meter (motorized type) TRHM-B10
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Brinell hardness test
- 306, 613, 1839 N
Digital low load Vickers Hardness tester TDVH-A10
- Test force
- 9.8 N, 49 N, 98 N, 196 N, 294 N, 490 N
- Hardness value symbol
- HV1, HV5, HV10, HV20, HV30, HV250
- Error range in display
- ± 3.0 %, ± 2.0 %
Portable Vibration Calibrator LPVC-A10
- Frequency (continually adjustable)
- 10 Hz to1280 Hz + 0.01 %
- Amplitude acceleration ( at 30m/s2 pk )
- 40 Hz to 320 Hz + 0.3 dB + 1 digit
- Amplitude velocity ( at 25mm / sec pk )
- 40 Hz to 320 Hz + 0.5dB +1 digit