TNRR-A10 is a No rotor rheometer where rubber sample is enclosed in mold cavity, maintained at test temperature. The mold cavity comes in two parts, where lower part (swing oscillations) determines strain as the reaction torque of the mold cavity (force). The PID controlled microprocessor technology controls and detects change in temperature. LCD screen display the real vulcanization curve and temperature curve, adjust the test data, store test results.
| Temperature tester | Room temperature to 200°C |
| Temperature display resolution | 0.1°C |
| Temperature control accuracy | ≤ ± 0.3°C |
| Rotor speed | 100 times/ min |
| Die cavity frequency | 1.7 Hz |
| Sway angle | ± 0.5°, ± 1°, ± 3° |
| Air compression | 0.5 MPa to 0.65 MPa |
| Ambient temperature | 0 to 35°C |
| Test result | Printed date, time, temperature, vulcanization curve, temperature curve ML, MH, ts1, ts2, t10, t50, Vc1, Vc2 |
| Display | Windows 7 + software |
| Torque range | 0 to 5 NM, 0 to 10 NM, 0 to 20 NM |
| Torque resolution | 0.001 NM |
| Product dimension | 1310 × 560 × 620 mm |
| Weight | 250 kg |
| Power supply | Single phase, 220 V ± 10%, 50 Hz |
- PID controlled microprocessor technology
- LCD Display
- Use of highly imported precision sensors
- Statistics, analysis, storage and comparison functions
- Can print automatic processing, calculations results
- Non curing viscometer monolithic rotor controlled
- User-friendly design appearance, easy to operate
- Supplied with data acquisition system
- Finds the vulcanization time for gelatin
No rotor rheometer is used to test vulcanization characteristics of rubber material across rubber industry for quality & research.
Rubber Testing Instruments
DIN abrasion tester TDAT-A10
- Test arm weight
- 2.5 N
- Additional Loads
- 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N,
- Idler
- 150 mm
Rubber Low Temperature Brittleness Tester TRBT-A11
- Temperature control range
- Room temperature to -70 ℃ (room temperature ≤ 25 ℃）
- Temperature accuracy
- ± 0.3 ℃
- Impact speed
- 0℃ to -30℃ around 2.5 ℃/min -30℃ to -40℃ around 2.5 ℃/min -40℃ to -70℃ around 2.0 ℃/min
Rubber low temperature brittleness tester TRBT-A10
- Temperature range
- -60°C to 0°C
- Temperature accuracy
- ± 0.5°C
- Impact speed
- 2 m/s ± 0.2 m/s
Rubber-weiss plasticity testing machine TRWM-A10
- Temperature range
- RT 50° to 300°
- Temperature accuracy
- ± 1°
- Measuring range
- 0.01 to 25 mm
Paper Testing Instruments
Whiteness and chromaticity tester TP-A10
- Sample (size) length
- Diameter ≥30 mm, Thickness ≤ 40 mm
- Measurement mode
- Diffuse reflection factor Rx, Ry, Rz, stimulus value Y10, X10, Z10, chromaticity coordinates x10, y10, z10; lightness L *, chroma a * b *, chroma C * ab, hue angle h * ab, dominant wavelength λd, excitement purity Pe, color difference ΔE * ab, lightness difference ΔL *, chroma difference ΔC * ab, hue difference ΔH * ab, Hunter system L , A, b
- Stability
- ≤ 0.1 within 30 min
Ink rubber tester TP-F10
- Sample size (L*B)
- 230×50 mm (can join short samples together)
- Rub pressure
- 20 ± 0.2 N
- Friction speed
- 43 times / min
Coefficient of friction tester TP-D10
- Measurement range
- 0.01 to 10 N
- Slider weight
- 200 g
- Slider size
- 63×63 mm
Plastic Testing Instruments
Charpy/ Izod Impact Tester TCI-A10
- Impact Speed & Energy (charpy)
- 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J
- Impact energy (Izod)
- 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J
- Resolution of impact energy
- 0.001 J
Melt flow Indexer TMFI-A10
- Measuring range
- 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density)
- Measuring rate
- 0.001 S
- Temperature range
- 50 to 400°C
Aging Oven TAO-A10
- The maximum temperature
- 300°C
- Temperature fluctuation
- Within ± 0.5°C
- Temperature uniformity
- Within ± 1°C
Vicat softening temperature & HDT machine TVHT-A10
- Operating temperature
- Ambient temperature to 300°C
- Heating rate
- 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min)
- Maximum temp. error with heating speed
- ± 5°C under 50°C/ h, ± 1°C under 120°C/ h
NDT Testing Instruments
Rockwell hardness meter TRHM-A10
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 0 to 30 S
Portable Vibration Calibrator LPVC-A10
- Frequency (continually adjustable)
- 10 Hz to1280 Hz + 0.01 %
- Amplitude acceleration ( at 30m/s2 pk )
- 40 Hz to 320 Hz + 0.3 dB + 1 digit
- Amplitude velocity ( at 25mm / sec pk )
- 40 Hz to 320 Hz + 0.5dB +1 digit
Digital Brinell hardness Tester TDBH-A10
- Test force
- 612.5 N, 980 N, 1225 N
- Brinell hardness test
- 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
- Hardness measuring area
- 8 to 650 HBW (hard metals steel ball)
Rockwell hardness meter TRHM-A11
- Preliminary test force
- 98 N
- Total test force
- 588, 980, 1471 N
- Total test force dwell time
- 1 to 30 S